Project Description

High speed steel scrap and re-melt ingots

Several very important factors allow high speed steel to work. The first is the type of metals used. Together, they can provide a heat resistance that can keep the metal hard even under extreme temperatures. High temperature treatment further helps the steel remain hard under extremely high temperatures. When tool steels contain a combination of more than 7% molybdenum, tungsten and vanadium, and more than 0.60% carbon, they are referred to as high speed steels

Below are a few of the alloys we trade in:
M35/ M2 / M3/M42/M4/M7/M10/T1/T4/T15/T21/T42

 

Typical High speed steel Alloy specifications we trade

Material Type Fe Co Cr Ni Fe Mo V W C others
M1 grade Bal 4.00 8.50 1.00 1.50 0.85
M2 grade Bal 4.00 5.00 2.00 6.00 1.0*
M3 grade Bal 5.00 5.00 2.40 6.00 1.05*
M4 grade Bal 4.00 4.50 4.00 5.50 1.30
M6 grade Bal 12.00 5.00 4.00
M7 grade Bal 4.00 8.75 2.00 1.75 1.00
M8 grade Bal 4.00 5.00 1.50 5.00 0.80 Cb 1.25%
M10 grade Bal 4.00 8.00 2.00 1.0*
M11 grade Bal 1.50 8.00 8.50 1.25 1.00 0.90
M15 grade Bal 5.00 4.00 3.50 5.00 6.50 1.50
M30 grade Bal 5.00 4.00 8.00 1.25 2.00 0.80
M33 grade Bal 8.00 4.00 9.50 1.15 1.50 0.90
M34 grade Bal 8.00 4.00 8.00 2.00 2.00 0.90
M35 grade Bal 5.00 4.00 5.00 2.00 6.00 0.80
M36 grade Bal 8.00 4.00 5.00 2.00 6.00 0.80
M41 grade Bal 5.00 4.25 3.75 2.00 6.75 1.10
M42 grade Bal 8.00 3.75 9.50 1.15 1.50 1.10
M43 grade Bal 8.25 3.75 8.00 1.60 2.75 1.20
M44 grade Bal 12.00 4.25 6.25 2.00 5.25 1.15
M45 grade Bal 5.50 4.25 5.00 1.60 8.00 1.25
M46 grade Bal 8.25 4.00 8.25 3.20 2.00 1.25
M47 grade Bal 5.00 3.75 9.50 1.25 1.50 1.10
M48 grade Bal 9.00 3.75 5.25 3.10 10.00 1.50
M50 grade Bal 4.00 4.25 1.00 0.80 Mn 0.25%/ Si 0.3%
M52 grade Bal 4.00 4.00 0.20 1.25 0.90
T1 grade Bal 4.00 0.95* 1.00 18.00 0.70
T2 grade Bal 4.00 0.95* 2.00 18.00 0.80
T3 grade Bal 4.00 3.00 18.00 1.05
T4 grade Bal 5.00 4.00 0.95* 1.00 18.00 0.75
T5 grade Bal 8.00 4.00 0.95* 2.00 18.00 0.80
T6 grade Bal 12.00 4.50 0.95* 1.50 20.00 0.80
T7 grade Bal 4.00 0.95* 2.00 14.00 0.75
T8 grade Bal 5.00 4.00 0.95* 2.00 14.00 0.75
T9 grade Bal 4.00 0.95* 4.00 18.00 1.20
T15 grade Bal 5.00 4.00 5.00 12.00 1.50